Superelastic carbon aerogels with anisotropic and hierarchically-enhanced cellular structure for wearable piezoresistive sensors.

Elastic carbon aerogels have promising applications in the field of wearable sensors. Herein, a new strategy for preparing carbon aerogels with excellent compressive strength and strain, shape recovery, and fatigue resistance was proposed based on the structure design and carbonization optimization of nanocellulose-based precursor aerogels. By the combination of directional freezing and zinc ion cross-linking, bacterial cellulose (BC)/alginate (SA) composite aerogels with high elasticity and compressive strength were first achieved. The existance of zinc ions also significantly improved the carbon retention rate and inhibited structural shrinkage, thus making the carbon aerogels retain ultra-high elasticity and fatigue resistance after compression. Moreover, the carbon aerogel possessed excellent piezoresistive pressure sensing performance with a wide detection range of 0-7.8 kPa, high sensitivity of 11.04 kpa-1, low detection limit (2 % strain), fast response (112 ms), and good durability (over 1,000 cycles). Based on these excellent properties, the carbon aerogel pressure sensors were further successfully used for human motion monitoring, from joint motion to and speech recognition.

Frost-resistant nanocellulose-based organohydrogel with high mechanical strength and transparency.

Improving mechanical strength and frost-resistance is an important research direction in the field of hydrogel materials. Herein, using bacterial nanocellulose (BC) as a reinforcing agent and polyvinyl alcohol (PVA) as a polymer matrix, a frost-resistant organohydrogel was constructed via the freezing-thawing method in a new binary solvent system of N, N-dimethylformamide and water (DMF-H2O), which was designed according to the Hansen Solubility Parameter. Owing to the solvent-induced crystallization effect that led to the enhanced 3D hydrogen bonding network during the freezing-thawing process, the optimal organohydrogel achieved excellent mechanical properties with the tensile strength of 2,974 kPa and the stretchability of 277 % at room temperature, respectively. In the visiblelight range, the organohydrogel demonstrated high transmittance. Moreover, the presence of a DMF-H2O binary solvent endows it with frost-resistance, retaining the tensile strength of 508 kPa and a stretchability of 190 % even at -70 °C, respectively. This kind of transparent, frost-resistant organohydrogel has potential uses in harsh settings due to its great mechanical strength.

Superelastic chitin nanofibril/chitosan aerogel for effective circulating and continuous oil-water separation.

Elastic and hydrophobic aerogels have received a lot of attention in dealing with the increasing oil pollution due to their recyclable properties. Herein, we present an ultralight and superelastic aerogel with highly oriented polygon structure based on chitin nanofibril (ChNF) and chitosan (CS) by directional freezing. The chemical cross-linking enables good mechanical strength at low aerogel density. After 500 compression-release cycles, the aerogel can retain the deformation recovery rate of 88 % in air, demonstrating the excellent resilience. The bio-based aerogel has high absorption capacity (52-114 g/g) for various oils and organic solvents, and it is able to achieve the absorption retention of 90 % even after 20 absorption-extrusion cycles. Moreover, owing to the good elasticity, the pore size of the aerogel can be adjusted by compression to selectively separate water-in-oil emulsions of different particle sizes with separation efficiencies higher than 99.5 %. The bio-based aerogel with good cycle performance has broad application prospects in the field of oil-water separation.